Review Article : Structures of phthalocyanine molecules on surfaces studied by STM

This review mainly focuses on progress recently achieved in the growth of phthalocyanine molecules on single-crystal surfaces of sub-monolayer up to few-monolayer thin films studied by scanning tunneling microscopy in our groups. On metallic surfaces such as Au(111), Ag(111) and Cu(111), molecular superstructures are determined by combining directional intermolecular interactions caused by symmetry reduction, molecule-substrate interactions and indirect long-range interactions due to quantum interference of surface state electrons. On semiconducting TiO 2 surface, molecular assembling structures are dictated by the strong molecule-substrate interaction. However, on insulating NaCl film, molecule-molecule interaction dominates over the molecule-NaCl coupling, leading to molecular growth behavior. Knowledge obtained from these studies would help people better understand the physicochemical properties of the phthalocyanine molecules at surfaces so that their new applications could be further explored and uncovered in the future.


I. INTRODUCTION
A phthalocyanine molecule is an organic macrocyclic compound with a 16-membered ring formed by alternate carbon and nitrogen.In a so-called non-substituted or metal-free phthalocyanine (H 2 Pc), the molecular center consists of two hydrogen atoms.The molecular center may likewise host a metal ion through coordinating d bonds with the central nitrogen atoms.Most metal elements in the periodic table can form coordination complexes (MPc, where M stands for a metal element) with phthalocyanines.Depending on the metal ion the molecular electronic and optical properties can be tailored while leaving its overall geometric structure virtually invariant.Phthalocyanines are widely used as pigments, dyes, nonlinear optical materials, enzyme-like catalysts, liquid crystals, sensitizers in photochemical reactions or photovoltaic cells, and photodynamic reagents for cancer therapy.For some applications, the molecules need to be deposited on supporting surfaces which subsequently interact with the molecules to affect the properties of the molecules.Therefore, understanding and controlling the growth of molecular films on surfaces are of fundamental importance in bettering their performance in these applications.In this context, many important investigations into structural and electronic properties of phthalocyanines have been achieved by using various surface science techniques.While a review of this wide field is beyond the scope of this article, we list a few most recent results obtained from ultraviolet 1, 2 and X-ray 3,4 photoelectron spectroscopy, inverse photoelectron spectroscopy, 5,6 electron energy loss spectroscopy, 7 near-edge X-ray absorption fine a E-mails: yongfengwang@pku.edu.cn,kaiwu@pku.edu.cnstructure, 8,9 normal incidence X-ray standing waves, 10 low-energy electron diffraction 11,12 and reflection high-energy electron diffraction. 13In particular, the scanning tunneling microscopy (STM) has been extensively used to explore the structural and electronic features of these molecules at the submolecular level in real space.  Therre already two excellent reviews about assemblies of phthalocyanines on surfaces. 57,58 colas Papageorgiou and co-workers presented physical aspects concerning the adsorption of phthalocyanine molecules deposited on semiconductor surfaces under ultrahigh vacuum conditions. 57oichiro Yoshimoto et al. summarized molecular assemblies of phthalocyanines and porphyrins noncovalently bounded to metal surfaces. 58Herein we present the growth of phthalocyanine molecules on the surfaces of several conducting metals, semiconducting TiO 2 and insulating NaCl thin films under ultrahigh vacuum conditions.These studies have been performed by STM in our groups in the past several years.On Ag(111) and Cu(111), molecular superstructures are determined by directional molecule-molecule attraction induced by symmetry reduction, indirect long-range interaction due to quantum interference of surface state electrons, 48 and molecule-substrate interaction.On the cross-linked TiO 2 (110)-(1×2) surface, CuPc-TiO 2 interaction dominates in molecular adsorption and assembly. 59On NaCl ultrathin film, SnPc tilts and grows in a Volmer-Weber mode, resulting in three-dimensional molecular nanocrystals formed at the initial stage, where the molecule-molecule interaction overtakes the molecule-NaCl coupling. 60

II. CoPc ON Cu(111)
CoPc exhibits a 4-fold rotational symmetry (C 4 ) in vacuum.A symmetry reduction from C 4 to C 2 is observed in STM images when CoPc adsorbs onto the 3-fold symmetric Cu(111) surface (Figure 1(a)).Similarly, SnPc adsorbed on Ag(111) also shows a C 2 symmetry in STM images (Figure 1(b)).Density functional calculations -with or without van der Waals (vdW) interactions -reveal that the atomic positions in the two perpendicular pairs of molecule ligands are different for both CoPc on Cu(111) 61 and SnPc on Ag(111) (Figure 1(c)).Consequently, the interaction and charge transfer between substrate and molecule should be different for the two molecular axes.The difference is highlighted by the colors marked on the ligand pairs.Green and red represent ligands along the close-packed and perpendicular direction, respectively.The green part appears as split protrusions, which corresponds to a reduced charge transfer between the substrate and molecule.In contrast, red lobes represent a large charge transfer and appear as non-split ones in STM images.The green-red cross is hereafter used to represent SnPc and CoPc with symmetry reduction.
The symmetry reduction has consequences for molecule-molecule dimers which are connected by weak C-H. . .3][64][65] Two different types of dimers (α and β) might be formed due to intermolecular attraction, which is induced by the aforementioned symmetry reduction (Figure 1(e)).Indirect long-range molecule-molecule interaction induced by quantum interference of surface state electrons via the substrate might lead to a third type of dimer (γ , Figure 1(e)).For SnPc-down molecules (which mean that the metal atom Sn in the non-planar SnPc molecule is in direct contact with the substrate), they prefer to form peculiar chains, where the molecular attraction between molecules occurs via split lobes (Figure 1(f), dimer α).At low coverages (θ < 0.5 ML), standing wave patterns around CoPc could be observed clearly (Figure 1(g)).
The surface charge density variations around CoPc molecules mediate long-range interactions among the molecules.Histograms of the nearest-neighbor separations of CoPc at low coverages show preferred distances of 2.1, 3.6, 5.0 and 6.5 nm.The 1.5 nm difference well matches half the Fermi wavelength of the Cu(111) surface state.
For a slightly higher coverage (θ > 0.5 ML), a uniform compression of the intermolecular distance is not observed in experiments, a scenario indicative of direct molecule-molecule interaction such as dipole-dipole 66 or electrostatic 67 repulsion.Rather, CoPc molecules form one-dimensional chains (Figure 1(i)), indicating that the surface state is essential in the structure formation of CoPc on Cu(111).Coverage-dependent experiments suggest the sequence of binding energies E(γ ) > E(α) > E(β).This sequence of energies is valuable for understanding self-assembly of CoPc on Cu(111).At a coverage of θ ≈ 0.5 ML, a long-range dispersed hexagonal pattern was formed (Figure 1(h)), where the distance between two molecules in dimer γ is 2.1 nm.This molecular pattern is similar  to Br island on Cu(111) 66 and Cu on Cu(111), 68 which are both stabilized by indirect long-range interaction induced by the Friedel-type oscillations of the local density of surface states around the adsorbates. 69,70 pon increasing the coverage up to 0.7 ML, an ordered array of chains is observed in STM images (Figure 2(a)), where the unique distance between two adjacent chains is again 2.1 nm.This array is composed of dimers α and γ .In dimer α, molecules are exclusively connected by green lobes.At the coverage of 0.8 ML, CoPc forms an unusual Kagome network (Figure 2(b)), which exhibits the highly symmetric plane group p31m.Once again, an intermolecular distance of 2.1 nm is experimentally observed, indicating that surface-state-mediated interaction plays an important role in the formation of the pattern.At 1.0 ML, CoPc forms close packed patterns in which molecules adopt two alternating adsorption configurations to reduce repulsion between red lobes (Figure 2(c)).

III. SnPc ON Ag(111)
Figure 3(a) displays two distinct images of SnPc on Ag(111). 46While one kind of molecule gives rise to a depression (central Sn atom points towards the surface, Sn-down) at its center, the other kind exhibits a protrusion (central Sn atom points towards vacuum, Sn-up).While Sn-up molecules are isolated from each other and from Sn-down molecules as well, Sn-down molecules agglomerate and form one-dimensional (1D) chains (Figure 1   repulsive interaction should be less stronger.At last, a net attraction, owing to C-H. . .N hydrogen bonds, remains and leads to agglomeration of the SnPc-down molecules. For SnPc molecules in the second molecular layer, the molecule-molecule coupling dominates the molecule-substrate interaction and molecules prefer to form two-dimensional islands at low coverages (Figure 3(b)).Homogeneous islands with a single orientation (SnPc-up or SnPc-down) are formed at the initial stage due to that the SnPc molecules are quite mobile on a molecule layer at room temperature and molecule-molecule hydrogen bonds are optimized in the process.
Starting from the third layer, the growth behavior changes from 2D layer-by-layer into threedimensional (3D) island growth (Figure 3(c)).At a coverage of 2.5 ML, a statistical analysis indicates that approximately 75% of molecules in the third layer are covered by molecules in the subsequent fourth layer.The third layer is mainly composed of SnPc-up molecules and the fourth layer consists of SnPc-down molecules.This double-layer island growth mode maintains until the coverage increases up to 6 ML (Figure 3(d)).All molecules in the topmost layer are SnPc-down molecules, with the SnPc-up ones staying in the layer underneath.

IV. CuPc ON THE CROSS-LINKED TiO 2 (110)-(1×2) SURFACE
In general, phthalocyanines on metallic substrates are mobile at room temperature and low coverages.Structural aspects are therefore accessible by low-temperature (LT) STM only.In contrast, on TiO 2 single dispersed CuPc molecules could be imaged at room temperature. 592][73] The adsorption of CuPc on TiO 2 is worthwhile to be investigated since it represents a model system for dye-sensitized solar cells and might be useful in purification of wastewater.The TiO 2 (110) surface is quite complicated and its structure strongly depends on the preparation process parameters such as the annealing temperature, duration time and ion bombardment. 74,75 he cross-linked TiO 2 (110)-(1×2) surface is the most favorable structure and most frequently used in experiments.Large-scale and high-resolution STM images of the cross-linked TiO 2 (110)-(1×2) surface are shown in Figures 4(a) and 4(b).Figure 4(c) shows the top and side view of the reconstructed surface structural model.This structure contains the link along 1-10 direction and Ti 2 O 3 added row along the [001] direction. 76igure 5 shows an STM image of CuPc deposited on the cross-linked TiO 2 (110)-(1×2) substrate.CuPc tends to locate at step edges, as shown in the inset in Figure 5. On the cross-linked TiO 2 (110)-(1×2) terrace, there are two main CuPc configurations which have been experimentally captured.In the first configuration, CuPc locates at the link site marked by the black rectangle.It shows a typically four-lobed shape, being similar to that of CuPc on metals where CuPc lies flat on the substrates.
Figure 6(a) (top view) and Figure 6(c) (side view) show the proposed adsorption model.It is known that nitrogen exhibits a strong interaction with the 5-fold coordinated Ti sites. 77It seems that CuPc is stabilized by the cooperative interactions between four molecular nitrogen atoms and

V. SnPc ON NaCl DOUBLE-LAYER FILMS SUPPORTED BY Au(111)
On metals and semiconductors, phthalocyanines prefer to lie flat on the surface and grow in a layer-island (Stranski-Krastanov) mode.However, Volmer-Weber growth of molecular nanocrystals occurs when SnPc adsorbs on NaCl double-layer films supported by Au(111). 59A constant-current STM image of Au(111) partially covered by a double-layer NaCl film is shown in Figure 7.The inset presents the schematic structure of NaCl.When deposited onto this NaCl-covered Au(111), the SnPc molecules first adsorb on the Au(111) surface.The growth behavior of SnPc on Au(111) is similar to that of SnPc on Ag(111).Once metal sites are fully occupied by SnPc, the molecules start to form the first layer on the NaCl film.

VI. SUMMARY
Self-assemblies of phthalocyanine molecules on various substrates from sub-monolayer to fewmonolayer thin films have been studied by STM in our groups.The variety of observed structures is dictated by the subtle balance between molecule-molecule and molecule-substrate interactions.On metal surfaces intermolecular coupling may be direct (e.g., dipole-dipole repulsion) or indirect (mediated by the conduction electrons).The resulting molecule assemblies (chains and two-dimensional islands) are formed owing to the rather high molecule mobility.Semiconductor surfaces tend to form strong chemical bonds to the molecule, which often results in mono-dispersed molecules.Ultrathin insulating films on metal surfaces decouple the molecules from the metal and as a result, the intermolecular interactions dominate to produce molecular nanocrystals.
Specifically, an ordered chain array and a Kagome lattice with the symmetry group p31m of CoPc on Cu(111) can be prepared by combining CoPc-Cu(111) interaction, directional CoPc-CoPc attraction induced by symmetry reduction, and indirect long-rang interaction caused by quantum interference of surface state electrons.For SnPc on Ag(111), two-dimensional layer-by-layer growth turns into three-dimensional island growth from the third layer on.Both SnPc-up and SnPc-down molecules coexist in the first and second layer.At higher coverages, the layers are composed of molecules with single orientation.The CuPc molecules deposited on the cross-linked TiO 2 (110)-(1×2) surface shows four adsorption structures and their appearances in STM images are dependent on their adsorption sites.On NaCl films, SnPc-SnPc interactions prevail over the SnPc-NaCl coupling, leading to that SnPc tilts on the surface and grows in a Volmer-Weber mode.
To summarize, STM has been widely used to study at the molecular and atomic levels the structural and electronic properties of the phthalocyanine molecules adsorbed at surfaces under various conditions.Accordingly, different approaches have been developed to control the adsorption and assembly of the phthalocyanine molecules at surfaces.In the past years, rapid progress has been made to understand the adsorption behavior of the phthalocyanine molecules by employing different types of substrates.This would certainly be helpful in fine-tuning the physicochemical properties of the ensembles involving the phthalocyanine molecules, a family of very important chemical molecules that have great applications in physics and related sciences.Obviously, such studies are still far away from completeness.Continuous effort has to be made to better the performance of the phthalocyanine molecules and explore their further and new applications in all walks.
Figure3(a) displays two distinct images of SnPc on Ag(111).46While one kind of molecule gives rise to a depression (central Sn atom points towards the surface, Sn-down) at its center, the other kind exhibits a protrusion (central Sn atom points towards vacuum, Sn-up).While Sn-up molecules are isolated from each other and from Sn-down molecules as well, Sn-down molecules agglomerate and form one-dimensional (1D) chains (Figure1(a)).The absence of SnPc-up aggregates might be due to

FIG. 6 .
FIG. 6. Top views of the proposed structural models of CuPc at (a) the link site and (b) the added row site on the cross-linked TiO2-(110)-(1×2) surface.Parts c and d are the corresponding perspective views of the proposed structures.In part a, the thick and thin arrows indicate possible coordination of the N atoms outside and inside the indole rings with nearby underlying Ti atoms in the substrate, respectively.In part b, thick and thin arrows indicate possible interactions of the H atoms in the benzene rings and the bridging N atoms in the N8 core with nearby O atoms and Ti atoms of the substrate, respectively.The long arrow in part d indicates the nonperfectly lined side indole rings pointing upward of two CuPc in two neighboring troughs along the [001] direction.Adapted with permission from Y. F. Wang et al., J. Phys.Chem.B 110, 17960 (2006).Copyright 2006 American Chemical Society.

Figure 8 (
Figure 8(a) shows an STM image of SnPc nano-island.The NaCl film around the molecules is atomically resolved (Figure 8(b)).The STM images of SnPc on NaCl with submolecular resolution are given in Figures 8(c) and 8(d), where only two isoindole groups of each SnPc molecule are visible as protrusions.This observation infers that the SnPc molecules tilt on NaCl with two isoindole groups pointing towards vacuum and the other two, towards NaCl.The energetically favorable adsorption configuration as revealed by supporting calculations consists of the SnPc molecular plane inclined by 65 • with respect to the surface normal of the double-layer NaCl film.This angle is in agreement with experimental observations.From the apparent height difference between subsequent molecular layers (0.5 nm) and the lateral size of a molecule (1.3 nm), an angle of arccos(0.5/1.3)≈ 67 • can be deducted.The dashed parallelogram in Figure 8(c) marks the unit cell in the top layer with parameters: 0.8 nm × 1.3 nm and an angle of 71 • between the unit cell vectors.A similar unit cell (0.8 nm × 1.4nm, 73 • ) was obtained by the theoretical calculation with EpiCalc.Molecular dynamics calculations indicate that the strong intermolecular interaction results in the molecular tilting within its molecular nano-crystals.Single SnPc molecule adopts a flat geometry with the molecular plane parallel to the surface.